Tire Marine Fender Casting PU Resin
dapatkan harga terbaruJenis pembayaran: | L/C,T/T |
Inkoterm: | FOB,CIF |
Min. Memesan: | 3 Ton |
Transportasi: | Ocean,Land,Air |
Pelabuhan: | Shanghai |
Jenis pembayaran: | L/C,T/T |
Inkoterm: | FOB,CIF |
Min. Memesan: | 3 Ton |
Transportasi: | Ocean,Land,Air |
Pelabuhan: | Shanghai |
Model No: A-1166,B-6003
Merek: Bahan Kimia Xuchuan
Tempat Asal: Cina
Jenis Dari: Resin Sintetis Dan Plastik
Brand Name: Xuchuan
Appearence: liquid
Model Number: A-1166,B-6003
Application: Tire(doule density), marine fender and shock absorption mat
Characteristic1: Good hydrolysis resistance and high resilience
Characteristic2: temperature has little effect on hardness
Bahan kimia roda pu
Karakteristik: resistensi hidrolisis yang baik dan ketahanan tinggi, suhu memiliki sedikit efek pada kekerasan
Aplikasi : ban (kepadatan ganda), fender laut dan matras penyerapan kejut
Roda Polyurethane Casting Resin Sifat Khas Matriks PU
Name of products | Appearance |
Viscoscity (mPa·s/40℃) |
Density (g·cm-³/40℃) |
Package (kg) |
A-1166 | (>25℃) Liqud | 700-1100 | 1.01-1.02 | 200 |
B-6003 | Yellowish Transparent liquid | 500-900 | 1.08-1.2 | 200 |
Bahan Bahan Pu Kustom Bahan Panaskan
A-1166 : dipanaskan sebelumnya pada 50 ℃ ~ 60 ℃ selama 8-12 jam
B-6003 : dipanaskan sebelumnya pada 60 ℃ ~ 70 ℃ selama 8-12 jam
Parameter pemrosesan tipikal & parameter reaksi
Items |
A/B Materials Temperatures (℃) |
Out-layer Mix ratio A+C/B (By weight) |
In-layer Mix ratio A+C/B (By weight) |
Cream Time (s) |
End of Rise Time (s) |
Out-layer Free Rise Foam Density (g/cm³) |
In-layer Free Rise Foam Density (g/cm³) |
Mold Temperature (℃) |
Demold Time (min) |
Parameter | 45-50/40-45 | 100/70 | 100/77 | 4-6 | 30-40 | 0.9-1.1 | 0.5-0.55 | 45-55 | 3-4 |
Konten Penambahan Catalyst (A: 200kg): Out-Layer --- C-2 4 ~ 4.5kg C-8 0.5 ~ 1kg
In-layer ----- C-2 3 ~ 3.5kg C-8 0.5 ~ 1.1kg
Konten penambahan hardener harus 400 ~ 500g/200kg sesuai dengan kenyataan
Konten penambahan hardener cf harus 0 ~ 3kg/200kg sesuai dengan kenyataan
Properti fisik
Items |
Molded Density (g/cm³)
|
Hardness (Shore A) |
Tear Strength (kN/m)
|
Tensile Strength (MPa) |
||||
Physical properties
|
Out-layer | In-layer | Out-layer | In-layer | Out-layer | In-layer | Out-layer | In-layer |
0.9-1.1 | 0.5-0.6 | 70-75 | 55-60 | 21-25 | 15-18 | 5.6-7.5 | 4.0-5.4 | |
Criterion |
ASTM D792 | ASTM D2240 | ASTM D624 | ASTM D412 |
Items | DIN abrasion(mm³) | Hydrolyzed properties 70℃*95% relative humidity Physical properties retention rate |
Ross Flexing -90°(-20℃) |
||
Out-layer | In-layer | 168 hours | 336 hours | 100000 times no crack | |
Physical properties | 70-100 | 100-200 | no significant decline | above 85% |
Data fisik ini diperoleh dengan menguji sampel kepadatan 6mm tebal dan 0,5 g/cm³
Kekerasan sampel pada suhu yang berbeda
Items |
Molded Density (g/cm³) |
20℃ | 10℃ | 0℃ | -4℃ | -10℃ | -20℃ |
Hardness (Shore A) |
0.5 | 50 | 50 | 51 | 51 | 52 | 54 |
Data yang tercantum di atas hanya untuk referensi. Data ini mengalami produksi praktis. Jika permintaan lain untuk sifat fisik, silakan hubungi kami.
Xuchuan Chemical yang didirikan pada tahun 2007, perusahaan terdaftar perusahaan RMB 500 juta. Produk utama adalah semua rentang poliol poliol, resin poliuretan untuk sepatu, resin poliuretan berbasis air dan pelarut untuk kulit buatan, perekat ikatan poliuretan dan perekat lebur panas poliuretan.
Sekarang Xuchuan memiliki 4 basis produksi modern, kapasitas produksi mencapai 630.000 ton per tahun, produk yang diekspor ke 32 negara dan wilayah di dunia.
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.
Fill in more information so that we can get in touch with you faster
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.