Cpu elastomer saringan bagian mesin penyegelan roller cincin
dapatkan harga terbaruJenis pembayaran: | L/C,T/T,D/P |
Inkoterm: | FOB,CFR,CIF |
Min. Memesan: | 1000 Kilogram |
Transportasi: | Ocean |
Pelabuhan: | Shanghai |
Jenis pembayaran: | L/C,T/T,D/P |
Inkoterm: | FOB,CFR,CIF |
Min. Memesan: | 1000 Kilogram |
Transportasi: | Ocean |
Pelabuhan: | Shanghai |
Model No: XCPU-E836
Merek: Bahan Kimia Xuchuan
Tempat Asal: Cina
Jenis Dari: Resin Sintetis Dan Plastik
Application: Rollers
CPU untuk elastomer
Deskripsi Produk
Polyester Prepolimer XCPU-E836
Prepolimer polisseter untuk cincin
1. Produk ini adalah poliol poliol dan toluena diisosianat (T-80) dalam sintesis prepolimer poliuretan poliester
2. Fitur: ketahanan aus yang sangat baik, ketahanan oli, sifat mekanik
3. Penggunaan: ayakan, bagian mesin, cincin penyegelan, roller pu dan produk lainnya
Prepolimer poliuretana poliether
Name of products
|
Appearances
|
Viscosity(mPa.s/85℃)
|
NCO% content
|
Package(kg)
|
XCPU-E836
|
solid
|
2000-2200
|
3.60-3.80
|
20 / 200
|
5、Mixing and Curing Conditions
|
|
|
|
|
|
|
||||||
MOCA Level
|
Recommended % Theory
|
Prepolymer Temperature
|
Curative Temperature
|
Pot Life
|
Demould Time
|
Post Cure Time
|
||||||
%
|
%
|
℃
|
℃
|
mins
|
@ 100°C (hrs)
|
@ 100°C (hrs)
|
||||||
10.8
|
95
|
75-85
|
110-120
|
4-4.5
|
1
|
10
|
Hardness
|
Shore A
|
86
|
Tensile Strength
|
MPa
|
49
|
100% Modulus
|
MPa
|
5.2
|
300% Modulus
|
MPa
|
9.7
|
Angle Tear Strength, Die C
|
kN/m
|
88
|
Trouser Tear Strength
|
kN/m
|
38
|
Elongation
|
%
|
680
|
Resilience
|
%
|
44
|
DIN Abrasion Resistance 10N
|
mm 3
|
44
|
Cured Specific Gravity
|
g/cm3
|
1.26
|
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.
Fill in more information so that we can get in touch with you faster
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.